Toluene diisocyanate manufacturer Knowledge Cashew nut shell liquid bio-based modified polyol FX-9007

Cashew nut shell liquid bio-based modified polyol FX-9007

Cashew nut shell liquid bio-based modified polyol FX-9007

Cashew nut shell liquid bio-based modified polyol FX -9007

Guangzhou Polycarbon provides a series of renewable polyol products for polyurethane formulations.

Cashew nut shell liquid products demonstrate excellent water resistance, low moisture sensitivity, and balanced mechanical strength.

Cashew nut shell liquid polyols provide excellent chemical resistance, especially alkali resistance.

Main markets include coatings, adhesives, potting, foam and composite materials.

Mechanical properties

Recipe

FX -9007/PMDI

= 100/40.3

Tensile strength(MPa)

17.3

ShaoDHardness

71

Lap shear strength, (MPa)

10.7

Elongation at break(%)

84

Tg(°C)

23.2

Cure conditions

Room temperature 7

Curing speed

Recipe

FX -9007/PMDI

= 100/40.3

Hard work(hours)at 25°C

4.5

Hard work(hours)at 5°C

17.3

Hard work(hours)at 0°C

22.7

Hydrolytic stability

Polyol samples, and polymerizationMDICure

NCOIndex=100)

FX-9007

Lap shear strength (MPa), Control sample

8.7

80°C/7 After Tianshui immersion test

Lap shear strength (MPa)

6.2

Lap shear strength decreases(%)

28.5

Lap shear strength (MPa), Control sample

8.7

80°C/7 After Tianshui immersion test

Lap shear strength (MPa)

6.2

Lap shear strength decreases(%)

28.5

This article is from the Internet, does not represent the position of Toluene diisocyanate reproduced please specify the source.https://www.chemicalchem.com/archives/17411

author:

Previous article
Next article
Contact Us

Contact us

+86 - 152 2121 6908

Online consultation: QQ交谈

E-mail: sales@newtopchem.com

Working hours: Monday to Friday, 9:00-17:30, closed on holidays
Follow wechat
Scan wechat and follow us

Scan wechat and follow us

Follow Weibo
Back to top
Home
E-mail
Products
Search